One of the key differences between the self-compacting concrete (SCC) and normal cement concrete (NCC) is the flowability property of SCC by it’s on weight. Most of the differences shown by SCC is due to this variation of flowability from the normal concrete.

Here the differences between SCC and normal concrete in terms of different fresh state properties, mix composition, and long-term properties are explained in the below section.

Difference between SCC and Normal Cement Concrete

The basic difference between self-compacting concrete and normal concrete are tabulated below.

Table.1: Difference between Self-Compacting Concrete and Normal cement Concrete

Sl.NoSelf-Compacting ConcreteNormal Cement Concrete
1Concrete has high flowability to undergo compaction by its own weightConcrete is compacted by external means of vibration
2High workabilityLess workable mix
3Workability gained through superplasticizers and viscosity modifying agentsWorkability gained through increased moisture content
4Addition of superplasticizer increase the bond between aggregate and cement matrixThe aggregate-cement matrix is weak
5Water Content is LowHigh Water Content
6Fines Content – Cement and Fine aggregate is highThe fines content is less compared to SCC
7Lower water content decreases the BleedingBleeding is high
8Increased fines content gives a homogeneous mix with less segregation issuesSegregation is higher
9Low Viscosity due to high fines contentHigh Viscosity
10SCC structures give good aesthetic finishAesthetic finish is not satisfactory
11Good choice for thick reinforcement worksNormal concrete are limited in thick reinforcement areas due to external compaction difficulties.

Fresh State Properties of SCC and Normal Cement Concrete

Following fresh state properties are used to bring the difference between SCC and NCC.

  1. Rheological Property
  2. Segregation
  3. Bleeding
  4. Strength Development
  5. Plastic Settlement
  6. Plastic Shrinkage
  7. Creep

1. Rheological Property

The superior properties reflected by SCC is due to its better rheology. The internal microstructure is more crack free and of high strength compared to normal concrete. More about rheology is explained by the workability properties.

SCC possess higher workability when compared with NCC. This is the property that enables the SCC to perform self-compaction. The workability in SCC is increased by the addition of superplasticizers.

The superplasticizers help to increase the property of fluidity. Fluidity in SCC is not obtained due to moisture, unlike NCC. Here the chemical reactions happening at the micro level of SCC results in increasing fluidity.

The figure-1 below shows the rheological properties of NCC and SCC. The variation is shown in terms of plastic viscosity and yield stress. When superplasticizers are added in lower volumes, the yield stress is lowered. This will bring a flowable concrete without segregation issues.

Rheological Properties of NCC and SCC(

Fig.1: Rheological Properties of NCC and SCC(Newman & Choo, 2003; Wallevik, 2003:23)

Higher amount of superplasticizers will result in high plastic viscosity and the yield stress is lowered. This creates flowable concrete with segregation issues.

2. Segregation

The Self-compacting concrete makes use of viscosity modifying agents (VMA) which creates problems when used in normal concrete. The VMA are pseudo polymers that helps in the reduction of aggregate segregation when compared to NCC.

Other than the VMA agent, the viscosity of SCC is high as it has a low water to powder ratio compared to NCC. This characteristic of SCC will inhibit the segregation.

3. Bleeding

Bleeding issues observed in SCC is less compared to normal concrete. This advantage of SCC is due to the lower water content and higher amount of fines. Higher binder content i.e. the cement, cement replacers and sand are causes of high fine content. A well-designed SCC mix can be properly handled without the issue of segregation and bleeding.

4. Strength Development

The strength development is similar to that of normal concrete (As per European Guidelines). As per the recommendations, maturity testing is a good way of controlling the strength development in SCC.

5. Plastic Settlement

The plastic settlement is formed in the concrete above the reinforcement in NCC structures. The use of viscosity modifying agent and increased powdered content in SCC helps to decrease the risk of plastic settlement cracks.

Higher flowability and plastic settlement in SCC prevents the occurrence of plastic settlement that is common in NCC. The cracks are ultimately filled with the increase in flowability.

6. Plastic Shrinkage

As the bleeding issues are less in SCC compared to normal concrete, the evaporation of moisture is controlled. Hence, proper curing of SCC is facilitated thus avoiding the chances of plastic shrinkage and resulted cracks.

7. Creep

Cement content in SCC is in high volume that results in high creep when compared with normal concrete.

Mix Composition of SCC and Normal Concrete

One of the major differences in materials used is the incorporation of superplasticizer in SCC mix which is ignored in normal concrete design. The SCC concrete can be developed with readily available materials. All other materials employed in SCC is similar to that of normal concrete but the difference is in the proportion added. The figure-3 below shows the variation of material constituents in self compacting concrete and normal cement concrete.

The mix composition of SCC v/s NCC

Fig.3: The mix composition of SCC v/s NCC; Image Courtesy: Okamura & Ouchi, 2003

In the figure above W = Water, C = Cement, G = Gravel, S = Sand, P= Powder (Cement replacements like fly ash, GGBS, silica fumes etc). It is observed that the aggregate content is decreased in SCC mix in order to increase the fraction of binder in the mix. Hence, the mix obtained with be rich with fines content. Normally, the increase in fine content implies the increase in surface area thus increasing the demand for moisture. But in SCC mix, this demand is met by the addition of superplasticizer.

Long Term Properties of SCC and Normal Concrete

The long-term properties will determine the structural durability of the concrete structure. Based on the studies conducted on SCC and NC in their hardened state, the following results were obtained:

  1. The compressive strength developed for SCC and normal concrete for same water-binder ratio are similar.
  2. The value of split tensile strength is higher in SCC compared to normal concrete
  3. The modulus of elasticity of self compacting concrete  is low compared when compared to normal concrete.

Read More: Self Compacting Concrete -Materials, Properties and Tests